A Comparative Analysis of Surface Characteristics of Enamel after Conventional Acid Etching and Er,Cr:YSSG Laser
Shahul-Hameed Faizee1, R Piradhiba2, N R Krishnaswamy3
1Professor and Head of the Department, Department of Orthodontics, Sathyabama Dental College and Hospital, Chennai.
Background:
To evaluate the influence of Erbium, Chromium:Yttrium-Scandium-Gallium-Garnet (Er,Cr:YSGG) laser irradiation (2W 15Hz, 2W 25Hz) on Penetration Depth, Surface Roughness, Surface Morphology and Etching Pattern of enamel and to compare it with conventional acid etching.
Material And Methods:
Sixty sound human premolars extracted for orthodontic reasons were used for this study. Penetration Depth and Surface Roughness between Acid Etched and Laser Etched Enamel were evaluated using Non-contact 3D- Profilometer .Surface Morphology and the Etching Pattern were evaluated using Field Emission - Scanning Electron Microscope.
Results:
On comparing the maximum depth and surface roughness values among all the three groups, highest was found in the acid-etched group, followed by the 2W 15Hz laser-etched group and the least was with the 2W 25Hz laser-etched group. The laser etching of enamel surface with an Er,Cr:YSGG laser system showed Type 3 etching pattern, whereas acid etched surface showed Type 1 etching pattern as described by Silverstone (1974).
Conclusions:
Er,Cr:YSGG laser irradiation produces favourable etching pattern and micro-irregularities that are suitable for resin penetration. Moreover, due to its decreased surface roughness and penetration depth, laser etching can significantly decrease the probability of formation of white spot lesions which is proved to be the potential disadvantage of conventional acid etching. Hence, laser etching can be preferred over the conventional phosphoric acid etching for orthodontic bonding. Key words:Laser, Er,Cr:YSGG, Surface Roughness, Etching Pattern,Penetration Depth,SEM, Laboratory Research, Acid etching.
More Related Videos
11:47Characterization of Surface Modifications by White Light Interferometry: Applications in Ion Sputtering, Laser Ablation, and Tribology Experiments
Published on: February 27, 2013
08:26Development of Amelogenin-chitosan Hydrogel for In Vitro Enamel Regrowth with a Dense Interface
Published on: July 10, 2014