Fast self-curing α-tricalcium phosphate/β-dicalcium silicate composites beneficial for root canal sealing treatment

α-tricalcium phosphate (α-TCP) and β-dicalcium silicate (β-C2S) have attracted much attention since these two types of self-curing Ca-phosphate and Ca-silicate are valuable biomaterials for bone defect or endodontic therapy. However, the injectable paste of their individual with high liquid/solid ratio is junior for root canal sealing due to very long self-setting time, low pH value and/or much volume shrinkage during paste-to-cement transformation.

Our studies evaluated the effect of biphasic ratio, liquid/solid ratio and pH condition of aqueous medium on setting time and mechanical strength of this biphasic composite cement, and also the hydroxyapatite re-mineralization potential and anti-microleakage level of the cements with different α-TCP/β-C2S ratio were explored in vitro. A control group free of paste filler was included in the extracted teeth model. Dentine re-mineralization and microleakage degree were observed by scanning electron microscopy and microCT reconstruction analysis.

It indicated that the weak acidic solution with pH value of 6.0 may produce a significantly shorter initial setting time (from 90 min to less 20 min) and expected final setting time (<150 min) for the biphasic composite (2:1 or 1:2) in comparison with the pure β-C2S. Notably, the phasic composites exhibited limited microleakage and induced hydroxyapatite mineralization in the dentine tubules. These hydraulic pastes also produced strong alkaline feature and appreciable compressive resistance (12-18 MPa) after setting for a very short time stage. Moreover, a link between the addition of α-TCP leading to fast re-mineralization reaction was established.

Our findings suggest that the appreciable self-setting and physicochemical properties adaption to root canal sealability make α-TCP/β-C2S composites as preferential candidates for endodontic treatments.