Study on laser-induced damage of TbBiIG crystal at 1064 nm

With the development of miniaturization of high-energy laser systems, a new Faraday rotator material must be studied to realize the miniaturization and integration of optical isolators. In this paper, high-quality (TbBi)₃Fe₅O₁₂ (TbBiIG) and Ca-doped (TbBi)₃Fe₅O₁₂ (Ca: TbBiIG) single crystal films with hundreds of microns thickness were grown by liquid phase epitaxy method on (111) oriented garnet substrate. The crystal structure, magneto-optical (MO), optical and laser induced damage properties were investigated in detail. We found that the (TbBi)₃Fe₅O₁₂ film has outstanding magneto-optical and laser-induced damage properties. Optical and MO properties indicate that TbBiIG films have a high specific faraday rotation angle of 1452 deg/cm at 1310 nm, and 2812 deg/cm at 1064 nm, absorption coefficient (α) is 5.63 cm^-1 and 15.7 cm^-1 at 1310 nm and 1064 nm, respectively. The laser-induced damage threshold (LIDT) of TbBiIG irradiated by a multi-frequency laser is 8.91 J/cm². The light absorption has a significant impact on LIDT value. Rare-earth ion doped iron garnet (RIG) material is a very potential MO material, which can greatly reduce the size and weight of optical isolators in the 1064 nm band.