Effect of Universal Adhesives on Long-term Bond Strength to Zirconia

To evaluate the effect of universal adhesives on the long-term bond strength to yttria-stabilized tetragonal zirconia polycrystal (Y-TZP).

Polyethylene tubes filled with composite cement containing 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) were adhesively luted to 60 fully sintered Y-TZP slabs (7 x 7 x 2 mm) with or without (control) previous application of a 10-MDP-based adhesive (All Bond Universal, Bisco) - ABU; Clearfil Universal Bond Quick, Kuraray Noritake - CUB; Scotchbond Universal Adhesive, 3M Oral Care - SUA) on the zirconia surface. The bonded specimens were stored in water for 24 h, 6 months, or 1 year and subjected to microshear bond strength testing. The data were analyzed by one-way ANOVA and Tukey's test (p < 0.05). The contact angle was measured after adhesive application to evaluate surface wettability. The adhesive-treated specimens were analyzed with x-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS) for chemical characterization.

The application of a 10-MDP-based adhesive significantly improved bond strength of composite cement to zirconia when compared to the control group (no adhesive application) (p < 0.05). One-year water storage significantly decreased bond strength for ABU- and CUB-bonded specimens, but not for SUA-bonded specimens. The analysis by XPS and ToF-SIMS showed peaks of carbon, phosphorus, and silicon in all adhesive-treated specimens.

One-year water storage affected the bond strength of composite cement to zirconia when All Bond Universal or Clearfil Universal Bond Quick were used.