Exceptional Strengthening Efficiency and Hardness of Ti/Mg-9Al-Zn-0.3Mn Matrix Composite

The involvement of magnesium matrix composite enhanced by metal particles, the development of low lattice mismatch interface, and the refining of particle size are all of great significance in improving strengthening efficiency. In this work, nano-crystalline Ti/Mg-9Al-Zn-0.3Mn composites were prepared by mechanical milling. The microstructure was characterized and the mechanical property was measured. After mechanical milling, the grain of the Mg matrix was refined to ~72 nm. Ti particles were smashed to submicron scale, and dispersed in the Mg matrix. In total, 68% of Ti particles were nano-scale and the average particle size was 133 nm. A nano-scale Mg₁₇Al₁₂ precipitate was found and the average particle size was approximately 44 nm. Meanwhile, coherent interfaces of Ti/Mg and Mg₁₇Al₁₂/Mg were observed, and it was found that the (101)Mg plane and (100)Ti plane inclined 12° and [044]Mg₁₇Al₁₂ was parallel to [010]Mg. The hardness of the milled Ti/Mg-9Al-Zn-0.3Mn composite was 1.98 GPa, 247% higher than the initial alloy. Milled Mg-9Al-Zn-0.3Mn alloy under the same preparation processing was used as a comparison, and the value of hardness was 1.53 GPa. Tiny Ti particles displayed excellent strengthening efficiency. Strengthening mechanisms of the milled Ti/Mg-9Al-Zn-0.3Mn composite were analyzed and the main strengthening mechanisms included the strengthening of grain boundary strengthening, Orowan strengthening, dislocation strengthening, solid solution strengthening and load-bearing strengthening, which accounted for 56.3%, 18.2%, 17.4%, 4.7% and 3.5%, respectively.