Halide-containing bioactive glasses enhance osteogenesis in vitro and in vivo

The application of bone substitutes to reconstruct bone defects is a strategy for repairing alveolar bone loss caused by periodontal disease. Bioactive glasses (BGs) are attractive synthetic bone substitutes owing to their abilities to degrade, form bone-like mineral and stimulate bone regeneration. Our previous studies showed that the incorporation of fluoride into alkali-free bioactive silicate glass promoted osteogenesis to some extent in vitro, while the incorporation of chloride facilitated glass degradation and accelerated the formation of hydroxyapatite. However, whether there is a synergistic effect of incorporating fluoride and chloride on further enhancement of osteogenesis and angiogenesis in vitro and in vivo was not known. Therefore, we synthesized three halide-containing BGs with fluoride only, or chloride only, or mixed fluoride and chloride, investigated their physicochemical properties and osteogenic and angiogenic effects both in vitro and in vivo. The results showed that the addition of both fluoride and chloride in a bioactive silicate glass could combine the structural roles of both, leading to a faster apatite formation than the glass with the presence of fluoride only and a more stable fluorapatite formation than the glass with the presence of chloride only, which formed hydroxyapatite upon immersion. The studied BGs were cytocompatible, as suggested by the cytotoxicity evaluation of hPDLSCs cultivated in the extracted BGs-conditioned culture media. More importantly, these BGs stimulated osteogenic differentiation of hPDLSCs without adding growth factors as indicated by the fact that BGs-conditioned media up-regulated the expression of BMP-2, OPN and VEGF of hPDLSCs and promoted the formation of bone nodules and collagen in vitro. By comparison, the incorporation of fluoride facilitated the expression of osteogenic-related biomarkers and bone nodule formation preferentially, while the incorporation of chloride induced the expression of angiogenic-related biomarkers and collagen formation. The in vivo investigation results demonstrated that the developed halide-containing BGs accelerated the process of bone regeneration, while the glass with mixed fluoride and chloride showed the most significant promotion effect among the three BGs. Therefore, our findings revealed a synergistic effect of incorporating fluoride and chloride into a BG on osteogenesis and angiogenesis in vitro and in vivo and highlighted the potential of fluoride and chloride containing bioactive glasses being bone substitutes for clinical use.