Aging resistance of highly translucent zirconia ceramics with rapid sintering

Rapid sintering technology has become one of the most direct methods for shortening the manufacturing time of zirconia restorations. This study aimed to explore the aging resistance of rapid-sintered 5 mol% yttria-partially-stabilized zirconia (5Y-PSZ).

Specimens were made from two types of 5Y-PSZ material and subjected to rapid sintering (RS) and conventional sintering (CS). After in vitro aging for 5 h, morphology observation, grain size measurement, and phase composition analysis were performed. The mechanical properties were evaluated by biaxial, three-point flexural tests, and the Vickers microhardness test. Results were analyzed by 3-way ANOVA.

Both the RS group and the CS group had a dense microstructure. The tested zirconia ceramics had different grain sizes, which were affected by the interaction between the sintering method and aging. Both groups revealed the same characteristic peaks of the cubic phase after aging. Regardless of the sintering method used, there was no significant difference in the mechanical properties of the tested zirconia before and after aging.

The rapid-sintered 5Y-PSZ materials had a microstructure, phase composition and mechanical properties similar to those of conventional sintered materials. The characteristics of the materials prepared using the two sintering methods did not change significantly after aging.