Characterization of Transparent Fluorapatite Ceramics Fabricated by Spark Plasma Sintering

Highly optically transparent polycrystalline fluorapatite ceramics with hexagonal crystal structures were fabricated via a liquid-phase synthesis of fluorapatite powder, followed by spark plasma sintering (SPS). The effect of sintering temperature, as observed using a thermopile, on the optical transmittance and microstructure of the ceramics was investigated in order to determine suitable sintering conditions. As a result, high optical transmittance was obtained in the SPS temperature range of 950-1100 °C. The highest optical transmittance was obtained for the ceramic sample sintered at 1000 °C, and its average grain size was evaluated at only 134 nm. The grain size dramatically increased with temperature, and the ceramics became translucent at SPS temperatures above 1200 °C. The mechanical and thermal properties of the ceramics were measured to evaluate the thermal shock parameter, which was found to be comparable to or slightly smaller than that of single-crystal fluorapatite. This transparent polycrystalline fluorapatite ceramic material should prove useful in a wide range of applications, for example as a biomaterial or optical/laser material, in the future. Furthermore, the knowledge obtained in this study should help to promote the application of this ceramic material.