The Damage Performance of Uncarbonated Limestone Cement Pastes Partially Exposed to Na₂SO₄ Solution

Pore structure and composition of cement paste are the main two factors in controlling the sulfate attack on concrete, but the influence of carbonization on pore structure and composition is often ignored in sulfate attack. Therefore, will the damage performance of concrete partially exposed to sulfate solution be different avoiding the alterations of pore structure and composition due to carbonation? In this paper, the cement pastes were partially immersed in 5 wt. % sodium sulfate solution, with N₂ as protective gas to avoid carbonation (20 ± 1°C, RH 65 ± 5%). Pore structures of cements were changed by introducing different contents of limestone powders (0 wt. %, 10 wt. %, 20 wt. %, and 30 wt. %) into cement pastes. The damage performance of the specimens was studied by ¹H NMR, XRD and SEM. The results showed that the immersion zone of pure cement paste under N₂ atmosphere remained intact while serious damage occurred in the evaporation zone. However, the damage of cement + limestone powders pastes appeared in the immersion zone rather than in the evaporation zone and cement pastes containing more limestone were more severely damaged. Compositional analysis suggested that the damage of the evaporation zone or the immersion zone was solely caused by chemical attack where substantial amount of gypsums and ettringites were filled in the pore volumes. Introduction of limestone powders led to the increase of the pore sizes and porosity of cement pastes, causing the damage occurred in the immersion zone not in the evaporation zone.