Effect of Mat Moisture Content, Adhesive Amount and Press Time on the Performance of Particleboards Bonded with...

The study evaluates the performance of laboratory, single-layered particleboards made out of fructose-hydroxymethylfurfural-bishexamethylenetriamine (SusB) adhesive as a sustainable alternative. Several production parameters such as mat moisture content (MMC), adhesive amount and press time were varied and their effect on the bonding efficiency investigated. The internal bond strength (IB) and thickness swelling after 24 h of water immersion (TS) were taken as evaluation criteria for the bonding efficiency. pMDI-bonded particleboards were produced as fossil-based, formaldehyde-free reference. Particleboard testing was complemented by tensile shear strength measurements and thermal analysis. It was found that the MMC has the highest impact on the internal bond strength of SusB-bonded particleboards. In the presence of water, the reaction enthalpy of the main curing reaction (occurring at 117.7 °C) drops from 371.9 J/mol to 270.5 J/mol, leading to side reactions. By reducing the MMC from 8.7%, the IB increases to 0.61 N/mm², thus surpassing P2 requirements of the European standard EN312. At a press factor of 10 s/mm, SusB-bonded particleboards have a similar IB strength as pMDI-bonded ones, with 0.59 ± 0.12 N/mm² compared to 0.59 ± 0.09 N/mm². Further research on the improvement of the dimensional stabilization of SusB-bonded PBs is needed, as the TS ranges from 30-40%.