Mechanical Behavior of Laminated Glass Polymer Interlayer Subjected to Environmental Effects

It is known that weathering action has a significant impact on polymer interlayer materials, and previous studies have evaluated certain aspects of weathering such as temperature, humidity, and UV radiation. In this paper, the environmental effect on the mechanical properties of the virgin and cured/processed polymer interlayer materials will be studied. Three polymer interlayer materials were focused, i.e., Polyvinyl butyral (PVB), Ethylene-vinyl acetate (EVA), and Ionomer (SG), due to their industrial interest. Testing setups were designed to apply the environmental effects and perform mechanical testing on the polymeric materials. Four environmental effects were studied, including water submersion (E1), constant high temperature (E2), cyclic temperature with low relative humidity (E3), cyclic temperature, and relative humidity (E4). After the exposure of these materials to these environmental effects, the samples were prepared and mechanically tested. Uniaxial tests were performed under static and high strain rates (around 45^-1). It was found that under dynamic load, the properties of EVA such as the strength, maximum strain, and the toughness were not significantly affected by the environmental effects. SG5000 properties were significantly affected.