A Large-Diameter Vascular Graft Replacing Animal-Derived Sealants With an Elastomeric Polymer

To assess the safety and efficacy of an experimental large-diameter vascular graft externally sealed with an elastomeric polymer when used as an interposition graft in the descending aorta of sheep.

The experimental vascular grafts as well as control gelatin sealed interposition grafts were inserted into the descending aorta of juvenile sheep. The grafts were assessed by time to hemostasis and blood loss during surgery and hematology and biochemistry panels at distinct time points. Magnetic resonance imaging (MRI) was performed at 3 and at 6 mo after surgery, after which the animals were euthanized and necropsies were carried out including macroscopic and microscopic examination of the grafts, anastomoses, and distal organs.

All animals survived the study period. There was no perceivable difference in the surgical handling of the grafts. The median intraoperative blood loss was 27.5 mL (range 10.0-125.0 mL) in the experimental group and 50.0 mL (range 10.0-75.0 mL) in the control group. The median time to hemostasis was 5.0 min (range 2.0-16.0 min) minutes in the experimental group versus 6.0 min (range 4.0-6.0 min) in the control group. MRI showed normal flow and graft patency in both groups. Healing and perianastomotic endothelialization was similar in both groups.

The experimental graft has a similar safety and performance profile and largely comparable necropsy results, in comparison to a commonly used prosthetic vascular graft, with the experimental grafts eliciting a nonadherent external fibrous capsule as the major difference compared to the control grafts that were incorporated into the periadventitia. Survival, hemostatic sealing, and hematologic and radiologic results were comparable between the study groups.