Creep Behavior of A356 Aluminum Alloy Reinforced with Multi-Walled Carbon Nanotubes by Stir Casting

Lightweight aluminum alloy components are often used to manufacture a variety of engineering components in many industries. In recent years, researchers have studied the effect of improving the mechanical properties of metal alloys by incorporating nano-carbon into its structure. In this study, the effect of the addition of 0.2, 0.5, and 1 wt% of multi-walled carbon nanotubes (MWCNTs) on the stress-strain behavior and creep phenomenon of an A356 aluminum alloy were studied. The effect of nickel coating on 0.2 wt% MWCNTs was also investigated. Samples were prepared using the stir-casting method. The results revealed that the grain size became finer when MWCNT nano-particulates were introduced. Although the MWCNTs were distributed homogeneously in the A356 matrix, as confirmed by FESEM analysis, there were some agglomerations observed in a specific area with dimensions smaller than 100 nm. Nevertheless, the addition of MWCNTs was found to be beneficial in enhancing the hardness of alloys containing 0.2 wt%, 0.2 wt% nickel-coated, 0.5 wt%, and 1 wt% MWCNTs by 9%, 24%, 32%, and 15%, respectively, as compared with the unreinforced A345 matrix. It was also found that the 0.5 wt% MWCNT-A356 matrix exhibited an improvement in the creep lifetime by more than two orders of magnitude.