Influence of Clinical Decontamination Techniques on the Surface Characteristics of SLA Titanium Implant

The study aims: 1. To perform diode laser, titanium (Ti) brush, and Ti curette treatment on sandblasted and acid-etched (SLA) Ti surfaces, with/without H2O2 and CHX, 2. To investigate the influence of decontamination techniques on implant surface topography and hydrophilicity. Diode laser, Ti brush, and Ti curette treatments were performed on the Grade 4 Ti discs, with/without treatment with 3% H2O2 solution or 0.2% CHX. Surface characteristics were investigated via SEM, optical profilometry, and water contact angle meter. SEM findings revealed flat and scratched areas when treated with Ti curette and Ti brush. For diode laser, SEM showed melting in specific areas. Ra and Rt values were lower in all test groups than in the control group (p < 0.05). The adjunctive chemical treatment showed negligible effects in SEM images and surface roughness measurements compared to laser and mechanical treatment-only groups. H2O2 treatment resulted in enhanced hydrophilicity in either treatment modalities with a significant difference compared to the negative control group (p < 0.05). In all test groups, the hydrophilicity was enhanced compared to the negative control group (p < 0.05). Diode laser treatment had the least disruptive effect on the Ti surface characteristics. The use of other mechanical methods caused significant alterations in the surface roughness.