Integrating a Ferroelectric Interface with a Well-Tuned Electronic Structure in Lithium-Rich Layered Oxide Cathodes...

Li-rich layered oxides (LLOs) are considered promising candidates for new high-energy-density cathode materials for next-generation power batteries. However, their large-scale applications are largely hindered by irreversible Li/O loss, structural degradation, and interfacial side reactions during cycling. Herein, we demonstrate an integration strategy that tunes the electronic structure by La/Al codoping and constructs a ferroelectric interface on the LLOs surface through Bi_0.5Na_0.5TiO₃ (BNT) coating. Experimental characterization reveals that the synergistic effect of the ferroelectric interface and the well-tuned electronic structure can not only promote the diffusion of Li⁺ and hinder the migration of O but also suppress the lattice volume changes and reduce interfacial side reactions at high voltages up to 4.9 V vs Li⁺/Li. As a result, the modified material shows enhanced initial capacities and retention rates of 224.4 mAh g^-1 and 78.57% after 500 cycles at 2.0-4.65 V and 231.7 mAh g^-1 and 85.76% after 200 cycles at 2.0-4.9 V at 1C, respectively.