Centimeter-Sized Piezoelectric Single Crystal of Chiral Bismuth-Based Hybrid Halide with Superior Electrostrictive
Kezheng Tao1, Bowen Zhang1, Qiang Li1
1Key Laboratory of Bioorganic Phosphorus Chemistry & Chemical Biology (Ministry of Education), Department of Chemistry, Tsinghua University, Beijing, 100084, P. R. China.
Abstract:
The lead-free hybrid perovskite piezoelectrics possess advantages of easy processing, light weight, and low-toxicity over inorganic ceramics. However, the lack of understanding in structure-property relationships hinders exploration of new molecular piezoelectric crystals with excellent performances. Herein, by introducing chiral α-phenylethylammonium (α-PEA+ ) cations into bismuth-based hybrid halides, centimeter-sized (R-α-PEA)4 Bi2 I10 and (S-α-PEA)4 Bi2 I10 single crystals with a superior piezoelectric voltage coefficient g22 of 309 mV m N-1 , are obtained. Structural rigidity in crystals leads to a remarkable electrostrictive coefficient Q22 of 25.8 m4 C-2 , nearly 20 times higher than that of poly(vinylidene fluoride) (PVDF), which is beneficial to improve piezoelectricity with the synergistic effect of chirality. Moreover, the as-grown crystals show outstanding phase stability from 173 K to ≈470 K. This work suggests a design strategy based on rigidity and chirality to exploit novel piezoelectrics among hybrid metal halides.