Antibacterial one-step self-etching dental adhesive with silver nanoparticles synthesized in situ
Yichun Wang1, Yashuang Ding1, Jie Deng2
1Department of Prosthodontics, Nanjing Stomatological Hospital, Medical School of Nanjing University, #30 Zhongyang Road, Nanjing, Jiangsu 210008, PR. China.
Objectives:
The objective of this study is to value the long-term antibacterial capability and adhesive properties of one-step self-etching dental adhesive containing silver nanoparticles (AgNPs) synthesized in situ.
Methods:
One-step self-etching adhesives with various weight percentages of silver 2-ethylhezanoate (0%, 0.05%, 0.10%, and 0.20%) were obtained by in-situ synthesis; the sizes and distribution of the AgNPs in resin were observed. The antibacterial effects of dentin-resin specimens were assessed by various test methods after being aged for 1 week to 1 year. The microtensile bond strength (μTBS) and interfacial nanoleakage (NL) were evaluated using extracted human teeth after being aged for 1 day and 1 year.
Results:
Uniform distribution of AgNPs in resin was observed in all experimental groups, and the average size was 4.71 nm-4.81 nm. All groups containing AgNPs showed significant antibacterial differences from the control group (P<0.05) over the ageing of 1 year. Although the increase of concentration tended to improve antibacterial activity, significant differences were not observed between the 0.10% and 0.20% groups (P>0.05). No significant differences were observed between all experimental groups and the control group in μTBS testing and NL testing at 1-day and 1-year time points (P>0.05).
Conclusions:
0.10% AgNPs synthesized in situ might be appropriate to impart a long-term antibacterial ability to the one-step self-etching adhesive, without affecting its adhesive performance.
Clinical Significance:
This study suggests that in-situ synthesis of AgNPs is an effective method to improve the antibacterial ability of dental adhesives with the potential to inhibit secondary caries.