Ba3.5Cu7.55In1.15Se9: A Wide-Bandgap Copper Indium Selenide Reveals Strong Luminescence and Third-Harmonic Generation
Yu-Hsuan Su1, Wei-Liang Chen2, Hye Ryung Byun3
1Department of Chemistry, National Cheng Kung University, Tainan70101, Taiwan.
Abstract:
A new copper indium selenide, Ba3.5Cu7.55In1.15Se9, was synthesized by the KBr flux reaction at 800 °C. The compound crystallizes with orthorhombic , a = 46.1700(12) Å, b = 4.26710(10) Å, c = 19.8125(5) Å, and Z = 8. The structural framework mainly consists of four sites of cubane-type defective M4Se3 (M = Cu, Cu/In) units with disordered Cu+/In3+ ions present at the part corner of each unit. The single crystal emits intense photoluminescence at 657 nm with a relative quantum yield (RQY) 0.2 times that of rhodamine 6G powder. The compound belongs to a direct band gap at 1.91 eV, analyzed by Tauc's plot, and the energy is close to the PL position. The Hall effect measurement on a pressed pellet reveals an n-type conductivity with a carrier concentration of 3.358 × 1017 cm-3 and a mobility of 24.331 cm2 V-1 s-1. Furthermore, the compound produces a strong nonlinear third-harmonic generation (THG), with an χS(3) value of 1.3 × 105 pm2/V2 comparable to 1.6 × 105 pm2/V2 for AgGaSe2 measured at 800 nm.
More Related Videos
Related Concept Videos
01:14Photoluminescence: Applications
01:23Photoluminescence: Fluorescence and Phosphorescence
A pair of electrons in a...
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human...
01:26Variables Affecting Phosphorescence and Fluorescence