NIR-to-NIR UCL/T₁-weighted MR/CT multimodal imaging by NaYbF₄:Tm@NaGdF₄:Yb-PVP upconversion nanoparticles

Multimodal imaging nanoprobes are urgently sought because they can integrate different imaging function into individual nanoplatform and provide more comprehensive and accurate information for the diagnosis of early-stage tumor. Lanthanide-based upconversion nanoparticles (UCNPs) are regarded as promising nanoplatforms to fabricate these probes. Herein, we firstly developed the active core-active shell structured NaYbF₄:Tm@NaGdF₄:Yb-PVP UCNPs with the average diameter of 13.23±0.96nm as multimodal imaging probes. These water-dispersible nanoprobes presented excellent near-infrared to near-infrared (NIR-to-NIR) upconversion luminescence (UCL) performance, which is favorable for optical bioimaging due to deeper tissue penetration and autofluorescence reduction. After coated with the NaGdF₄:Yb active shell, the UCL emission intensity at 800nm increased by 7.2times. These nanoprobes exhibited a desirable longitudinal relaxivity (r₁=3.58L/(mmols)) and strong X-ray attenuation property (58.84HUL/g). The cytotoxicity assessment, histology analysis and biodistribution study revealed that NaYbF₄:Tm@NaGdF₄:Yb-PVP UCNPs had relatively low cytotoxicity and negligible organ toxicity. These UCNPs were applied for NIR-to-NIR UCL imaging in vivo. More importantly, the detection of small tumor was successfully achieved under T₁-weighted MRI and CT imaging modalities after intravenous injection of these UCNPs. These results revealed that NaYbF₄:Tm@NaGdF₄:Yb-PVP UCNPs could serve as promising NIR-to-NIR UCL/MRI/CT trimodal imaging probes.