Effect of Mg Addition and PMMA Coating on the Biodegradation Behaviour of Extruded Zn Material

Although zinc (Zn) is one of the elements with the greatest potential for biodegradable uses, pure Zn does not have the ideal mechanical or degrading properties for orthopaedic applications. The current research aims at studying the microstructure and corrosion behaviour of pure Zn (used as a reference material) and Zn alloyed with 1.89 wt.% magnesium (Mg), both in their extruded states as well as after being coated with polymethyl methacrylate (PMMA). The grafting-from approach was used to create a PMMA covering. The "grafting-from" method entails three steps: the alkali activation of the alloys, their functionalization with an initiator of polymerization through a phosphonate-attaching group, and the surface-initiated atom transfer radical polymerisation (SI-ATRP) to grow PMMA chains. Electrochemical and immersion corrosion tests were carried out in a simulated body fluid (SBF), and both confirmed the enhanced corrosion behaviour obtained after coating. The electrochemical test revealed a decrease in the degradation rate of the alloy from 0.37 ± 0.14 mm/y to 0.22 ± 0.01 mm/y. The immersion test showed the ability of complete protection for 240 h. After 720 h of immersion, the coated alloy displays minute crevice corrosion with very trivial pitting compared to the severe localized (galvanic and pitting) corrosion type that was detected in the bare alloy.