Improvement in Processability for Injection Molding of Bisphenol-A Polycarbonate by Addition of Low-Density

Yuki Kuroda1, Ken-Ichi Suzuki1, Genzo Kikuchi1

  • 1Polymer Materials Research Laboratory, Tosoh Corporation, 1-8 Kasumi, Yokkaichi 510-8540, Mie, Japan.

Materials (Basel, Switzerland)
|January 21, 2023
PubMed

Keywords:
injection moldinglow-density polyethylenepolycarbonatepolymer blendshear viscosity

More Related Videos

Application of a Coupling Agent to Improve the Dielectric Properties of Polymer-Based Nanocomposites06:34

Application of a Coupling Agent to Improve the Dielectric Properties of Polymer-Based Nanocomposites

Published on: September 19, 2020

5.9K
Rapid and Low-cost Prototyping of Medical Devices Using 3D Printed Molds for Liquid Injection Molding10:43

Rapid and Low-cost Prototyping of Medical Devices Using 3D Printed Molds for Liquid Injection Molding

Published on: June 27, 2014

20.0K

Related Concept Videos

Polymer Classification: Architecture01:14

Polymer Classification: Architecture

Polymers are classified as linear or branched on the basis of their chain architecture. The polymer chains in linear polymers have a long chain-like structure with minimal to no branching at all. Even if a polymer features large substituent groups on the monomer, which appear as branches to the skeleton, it is not considered a branched polymer. A branched polymer contains secondary polymer chains that arise from the main polymer chain. The branching occurs when the polymer growth shifts from...
2.8K
Types of Step-Growth Polymers: Polyesters01:20

Types of Step-Growth Polymers: Polyesters

The introduction of polyesters has brought major development to the textile industry. The wrinkle-free behavior of polyester blends has eliminated the need for starching and ironing clothes.
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the...
2.3K
Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
2.5K
Plasticizers01:31

Plasticizers

Water-reducers, or plasticizers, are chemical admixtures used in concrete to improve strength and workability. These additives reduce the water-cement ratio without compromising workability, lower the cement content while maintaining the same workability, or increase workability to assist concrete placement in inaccessible areas.
Plasticizers function by using surface-active agents to create repulsive electrostatic forces between cement particles. This dispersion enhances the concrete's...
104
Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...
3.6K
Free-Radical Chain Reaction and Polymerization of Alkenes02:35

Free-Radical Chain Reaction and Polymerization of Alkenes

The conversion of alkenes to macromolecules called polymers is a reaction of high commercial importance. The structure of the polymer is defined by a repeating unit, while the terminal groups are considered insignificant. The average degree of polymerization represents the number of repeating units in the polymer molecule and is denoted by the subscript n.
8.0K