Study on mechanical properties and damage characteristics of rice straw fiber-reinforced cemented tailings backfill...

Low-cost and underutilized plant fibers can affect the mechanical behavior of cementitious materials such as cemented tailings backfill (CTB). This paper attempts to explore the mechanical properties and damage evolution characteristics of rice straw fiber (RFS)-reinforced CTB (RSFCTB) from the perspective of energy. A series of mechanical and microscopic tests were carried out on CTB and RSFCTB samples. On this basis, the energy evolution law and of the filling body under different stress paths were analyzed. Meanwhile, a damage variable based on dissipation energy was established, and the damage evolution process of the filling body was discussed. The results show that uniaxial compressive strength (UCS) of filling body first grew and then dropped with the enhancement of RSF content, and indirect tensile strength (ITS) was positively correlated with RSF content. Scanning electron microscope showed that RSF was encapsulated by hydration products, which promoted the bridging effect of RSF. The bridging effect of RSF improved the integrity of RSFCTB after compression failure and resulted in bending and asymmetric tensile cracks after tensile failure. The energy storage limit and dissipation energy of the filling body under different stress paths were enhanced due to the incorporation of RSF. The damage curve based on dissipation energy showed three stages of slow, steady, and fast damage under compressive loading. The damage curve of RSFCTB was located below CTB depending on the crack arresting effect of RSF. Moreover, the damage curve under tensile load shows three stages: slow, stable damage, and sudden increase in damage. The damage value of RSFCTB at the mutation point was increased, and the ability of RSFCTB to resist tensile damage was enhanced. The energy evolution and acoustic emission parameters were combined, and their development trends were similar, which proved that it was reasonable to characterize the damage of filling body based on the dissipated energy.