Highly Stable Electrochemical Supercapacitor Performance of Self-Assembled Ferromagnetic Q-Carbon

Novel phase Q-carbon thin films exhibit some intriguing features and have been explored for various potential applications. Herein, we report the growth of different Q-carbon structures (i.e., filaments, clusters, and microdots) by varying the laser energy density from 0.5 to 1.0 J/cm² during pulsed laser annealing of amorphous diamond-like carbon films with different sp³-sp² carbon compositions. These unique nano- and microstructures of Q-carbon demonstrate exceptionally stable electrochemical performance by cyclic voltammetry, galvanostatic charging-discharging, and electrochemical impedance spectroscopy for energy applications. The temperature-dependent magnetic studies (magnetization vs magnetic field and temperature) reveal the ferromagnetic nature of the Q-carbon microdots. The saturation magnetization and coercive field values decrease from 132 to 14 emu/cc and 155 to 92 Oe by increasing the temperature from 2 to 300 K, respectively. The electrochemical performances of Q-carbon filament, cluster, and microdot thin-film supercapacitors were investigated by two-electrode configurations, and the highest areal specific capacitance of ∼156 mF/cm² was observed at a current density of 0.15 mA/cm² in the Q-carbon microdot thin film. The Q-carbon microdot electrodes demonstrate an exceptional capacitance retention performance of ∼97.2% and Coulombic efficiency of ∼96.5% after 3000 cycles due to their expectational reversibility in the charging-discharging process. The kinetic feature of the ion diffusion associated with the charge storage property is also investigated, and small changes in equivalent series resistance of ∼9.5% and contact resistance of ∼9.1% confirm outstanding stability with active charge kinetics during the stability test. A high areal power density of ∼5.84 W/cm² was obtained at an areal energy density of ∼0.058 W h/cm² for the Q-carbon microdot structure. The theoretical quantum capacitance was obtained at ∼400 mF/cm² by density functional theory calculation, which gives an idea about the overall capacitance value. The obtained areal specific capacitance, power density, and impressive long-term cyclic stability of Q-carbon thin-film microdot electrodes endorse substantial promise in high-performance supercapacitor applications.