Magnetic Anisotropies and Exchange Bias of Co/CoO Multilayers with Intermediate Ultrathin Pt Layers
Dimitrios I Anyfantis1, Camillo Ballani2, Nikos Kanistras1,2
1Department of Materials Science, School of Natural Sciences, University of Patras, 26504 Patras, Greece.
Abstract:
Co/CoO multilayers are fabricated by means of radio-frequency magnetron sputtering. For the formation of each multilayer period, a Co layer is initially produced followed by natural oxidation. Platinum is used not only as buffer and capping layers, but also in the form of intermediate ultrathin layers to enhance perpendicular magnetic anisotropy. Three samples are compared with respect to the magnetic anisotropies and exchange bias between 4-300 K based on superconducting quantum interference device magnetometry measurements. Two of the multilayers are identical Co/CoO/Pt ones; one of them, however, is grown on a Co/Pt "magnetic substrate" to induce perpendicular magnetic anisotropy via exchange coupling through an ultrathin Pt intermediate layer. The third multilayer is of the form Co/CoO/Co/Pt. The use of a "magnetic substrate" results in the observation of loops with large remanence when the field applies perpendicular to the film plane. The CoO/Co interfaces lead to a significant exchange bias at low temperatures after field cooling. The largest exchange bias was observed in the film with double Co/CoO/Co interfaces. Consequently, significant perpendicular anisotropy coexists with large exchange bias, especially at low temperatures. Such samples can be potentially useful for applications related to spintronics and magnetic storage.
Related Concept Videos
01:27Biasing of Metal-Semiconductor Junctions
In Schottky junctions, where the semiconductor is n-type, applying a positive voltage to the metal relative to the semiconductor reduces its Fermi...
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human...
01:31Magnetic Susceptibility and Permeability
When diamagnetic materials are placed under an external magnetic field, the moments opposite to the field are induced. Hence, the susceptibility for diamagnets has a minimal negative value of 10-5–10-6. Since...
01:27π Electron Effects on Chemical Shift: Overview
01:31Ferromagnetism
01:23Magnetic Field due to Moving Charges
Consider a point charge moving with a constant velocity. Like the electric field, the magnetic field at any point is directly proportional to the magnitude of the charge and inversely proportional to the square of the distance between the source point and the field point. However, unlike the electric field, the magnetic field is always perpendicular to the plane containing the line...