Mechanical Behaviors of Microwave-Assisted Pyrolysis Recycled Carbon Fiber-Reinforced Concrete with Early-Strength...

This study aimed to investigate the mechanical performance of early-strength carbon fiber-reinforced concrete (ECFRC) by incorporating original carbon fiber (OCF), recycled carbon fiber (RCF), and sizing-removed carbon fiber (SCF). Compressive, flexural, and splitting tensile strength were tested under three fiber-to-cement weight ratios (5‱, 10‱, and 15‱). The RCF was produced from waste bicycle parts made of carbon fiber-reinforced polymer (CFRP) through microwave-assisted pyrolysis (MAP). The sizing-removed fiber was obtained through a heat-treatment method applied to the OCF. The results of scanning electron microscopy (SEM) analysis with energy dispersive X-ray spectrometry (EDS) indicated the successful removal of sizing and impurities from the surface of the RCF and SCF. The mechanical test results showed that ECFRC with a 10‱ fiber-to-cement weight ratio of carbon fiber had the greatest improvement in its mechanical strengths. Moreover, the ECFRC with 10‱ RCF exhibited higher compressive, flexural, and splitting tensile strength than that of benchmark specimen by 14.2%, 56.5%, and 22.5%, respectively. The ECFRC specimens with a 10‱ fiber-to-cement weight ratio were used to analyze their impact resistance under various impact energies in the impact test. At 50 joules of impact energy, the impact number of the ECFRC with SCF was over 23 times that of the benchmark specimen (early-strength concrete without fiber) and was also greater than that of ECFRC with OCF and RCF.