Effect of the Deposit Temperature of ZnO Doped with Ni by HFCVD

The effect of the deposit temperature of zinc oxide (ZnO) doped with nickel (Ni) by hot filament chemical vapor deposition (HFCVD) technique is reported in this work. The technique allows depositing ZnO:Ni in short intervals (1 min). A deposit of undoped ZnO is used as a reference sample. The reference sample was deposited at 500 °C. The ZnO:Ni samples were deposited at 500 °C, 400 °C, 350 °C, and 300 °C. The samples were studied using structural, morphological, and optical characterization techniques. The Ni incorporation to the ZnO lattice was verified by the shift of the X-ray diffraction peaks, the Raman peaks, the band gap, and the photoluminescence measurements. It was found that the deposit temperature affects the structural, morphological, and optical properties of the ZnO:Ni samples too. The structure of the ZnO:Ni samples corresponds to the hexagonal structure. Different microstructures shapes such as spheres, sea urchins, and agglomerate were found in samples; their change is attributed to the deposit temperature variation. The intensity of the photoluminescence of the ZnO:Ni improves concerning the ZnO due to the Ni incorporation, but it decreases as the deposit temperature decreases.