Synthesis and Characterization of Electrospun Carbon Nanofibers from Polyacrylonitrile and Graphite Nanoplatelets

Sol-gel electrospinning process was used to prepare electrospun carbon nanofibers (ECNFs) from polyacrylonitrile and graphite nanoplatelets. The nanofibers of as-electrospun carbon were calcinated in argon from room temperature to 500 °C for 1h. Scanning and transmission electron microscopy with energy-dispersive X-ray spectroscopy and X-ray diffractometry (XRD) were used to characterize the synthesized ECNFs. The smooth ECNFs with a diameter of 129 ± 43 nm comprised conical platelets of 30-200 µm length. The plane-layered nanofibers contained crystallites along the long fiber axis and were mainly parallel.