Effect of different root canal irrigants on push-out bond strength of two novel root-end filling materials

The aim of this in vitro study was to evaluate push-out bond strength of different root-end filling materials using various irrigant solutions.

A push-out bond strength test was performed to evaluate the bond strength of two experimental root-end filling materials: namely, nano-hybrid mineral trioxide aggregate (MTA) and polymethyl methacrylate (PMMA) cement filled with 20% weight nano hydroxyapatite (nHA) fillers compared to conventional MTA. The irrigant solutions employed were sodium hypochlorite (NaOCl) in concentrations 1%, 2.5% and 5.25% and 2% chlorhexidine gluconate (CHX) followed by application of 17% ethylene diamine tetra-acetic acid (EDTA). A freshly extracted sixty single-rooted human maxillary central incisors were used. The crowns were removed, the canal apex was widened to simulate immature teeth. Each type of irrigation protocols was performed. After application and setting of the root-end filling materials, a slice of one mm thickness was cut transversely from the apical end of each root. Specimens were stored for 1 month in artificial saliva and were subjected to a push-out test to evaluate the shear bond strength. Data were analyzed using two-way ANOVA and Tukey test.

The experimental nano-hybrid MTA showed the highest significant push-out bond strength values when irrigated by NaOCl at several concentrations (1%, 2.5% and 5.25%) (P< 0.05). Meanwhile, irrigation with 2% CHX resulted in highest bond strength values in nano-hybrid white MTA (18 MPa) and PMMA filled with 20% weight nHA (17.4 MPa) with nonsignificant difference between them (p = 0.25). In each root-end filling material, irrigation with 2% CHX led to the highest significant bond strength, followed by NaOCl 1%, while the least significant bond strength was produced after irrigation with NaOCl 2.5% and 5.25% (P< 0.05).

Considering the limitations of this study, it may be concluded that the application of 2% CXH and 17% EDTA provides superior push-out bond strength to root canal dentin compared with irrigation with NaOCl irrigants and 17% EDTA, experimental nano-hybrid MTA root-end filling material provides enhanced shear bond strength than conventional micron-sized MTA root-end filling material.