Characterizing the viscoelastic properties of the anterolateral ligament and grafts commonly used in its...

Current anatomic anterolateral ligament reconstruction is typically performed using either a gracilis tendon or an iliotibial band graft based on their quasi-static behavior. However, there is limited knowledge about their viscoelastic behaviors. This study aimed to characterize the viscoelastic properties of the anterolateral ligament, distal iliotibial band, distal gracilis tendon and proximal gracilis tendon for graft material choice in anterolateral ligament reconstruction.

All the tissues were harvested from thirteen fresh-frozen cadaveric knees and subjected to preconditioning (3-6 MPa), sinusoidal cycle (1.2-12 MPa), dwell at constant load (12 MPa), and load to failure (3%/s). The quasi-static and viscoelastic properties of the soft tissues were computed and compared using a linear mixed model (p < 0.05).

The hysteresis of anterolateral ligament (mean:0.4 Nm) was comparable with gracilis halves (p > 0.85) but iliotibial band (6 Nm) was significantly higher (p < 0.001,ES = 6.5). In contrast, the dynamic creep of anterolateral ligament (0.5 mm) was similar to iliotibial band (0.7 mm, p > 0.82) whereas both gracilis halves were significantly lower (p < 0.007,ES > 1.4). The elastic modulus of anterolateral ligament (181.4 MPa, p < 0.001,ES > 2.1) was the lowest compared to the grafts materials (distal gracilis tendon:835 MPa, distal gracilis tendon:726 MPa, iliotibial band:910 MPa). Additionally, the failure load of the anterolateral ligament (124.5 N, p < 0.001,ES > 2.9) was also the lowest.

The mechanical properties of the gracilis halves and iliotibial band were significantly different from anterolateral ligament, except for hysteresis and dynamic creep, respectively. Our findings showed that the gracilis halves may be a more appropriate graft choice for anterolateral ligament reconstruction due to its low energy dissipation and permanent deformation under dynamic loads.