Fly ash boosted electrocatalytic properties of PEDOT:PSS counter electrodes for the triiodide reduction in...

Fly ash solid waste from a power plant was applied in a solar cell application for the first time. A doctor blade was used to coat FTO-glass with a composite film of mixed fly ash and PEDOT:PSS (FP). XRD, FTIR, SEM, EDX, and BET analyses were used to elucidate the crystal structure, morphology, and functional groups of fly ash in the current research. A significantly high efficiency solar cell was fabricated utilizing fly ash. CV, Tafel, and EIS analyses indicated a decrease in charge transfer resistance and an increased catalytic activity in the counter electrodes. The performance of DSSCs made from FP counter electrodes varied depending on the percentage of fly ash particles present. Fly ash mixed with PEDOT:PSS in a concentration ratio of 2:5 g/mL showed a high efficiency of 4.23%, which is comparable to Pt DSSC's (4.84%). Moreover, FP-2:5 presented a more highly efficient electrode than counter electrodes made from PEDOT:PSS mixed with MoO (3.08%) and CoO (3.65%). This suitability of this low-cost CE material for use in DSSCs has been established.