Improved hydrophobicity, antibacterial and mechanical properties of polyvinyl alcohol/quaternary chitosan composite...

Polyvinyl alcohol (PVA) and chitosan (CS) are attractive polymeric feedstocks for developing eco-environmental materials. In this work, a biodegradable and antibacterial film was developed based on PVA blending with different long-chain alkyl and different contents of quaternary chitosan through solution casting, in which quaternary chitosan not only acted as an antibacterial agent but also improved hydrophobicity and mechanical properties. A novel peak appeared at 1470 cm^-1 in Transform Infrared Spectroscopy (FTIR) and a new CCl bond spectral peak at 200 eV in X-ray photoelectron spectroscopy (XPS) spectra suggested that CS was successfully modified by quaternary. Besides, the modified films have better antibacterial effects against Escherichia (E. coli) and Staphylococcus (S. aureus) and present stronger antioxidant properties. Optical properties demonstrated that the light transmittance on both UV and visible light showed a decreasing trend with the increase of the quaternary chitosan contents. Whereas the composite films have enhanced hydrophobicity than PVA film. Furthermore, the composite films had higher mechanical properties, in which Young's modulus, tensile strength, and elongation at break were 344.99 MPa, 39.12 MPa, and 507.09 %, respectively. This research demonstrated that the modified composite films could extend the shelf of life on antibacterial packaging.