Synthesis and characterization of low surface energy thermoplastic polyurethane elastomers based on

Jie Sun1, Xiaobin Zou1, Zhiqian Xu1

  • 1School of Materials Science and Engineering, Beijing Institute of Technology Beijing 100081 China gzandlsy@bit.edu.cn.

RSC Advances
|April 20, 2023
PubMed

More Related Videos

Drawing and Hydrophobicity-patterning Long Polydimethylsiloxane Silicone Filaments07:56

Drawing and Hydrophobicity-patterning Long Polydimethylsiloxane Silicone Filaments

Published on: January 7, 2019

9.0K
Synthesis of Terpolymers at Mild Temperatures Using Dynamic Sulfur Bonds in PolyS-Divinylbenzene09:16

Synthesis of Terpolymers at Mild Temperatures Using Dynamic Sulfur Bonds in PolyS-Divinylbenzene

Published on: May 20, 2019

7.8K

Related Concept Videos

Characteristics and Nomenclature of Homopolymers01:00

Characteristics and Nomenclature of Homopolymers

Polymers that are made up of identical monomer units are called homopolymers. Only one repeating unit is involved in the construction of the homopolymer structure. For example, as depicted in Figure 1, polypropylene is a homopolymer constituted of propylene monomers. Here, the only repeating unit in the polymer chain is propylene.
3.1K
Olefin Metathesis Polymerization: Overview01:13

Olefin Metathesis Polymerization: Overview

Recently, the development of olefin metathesis polymerization advanced the field of polymer synthesis. Simply put, the reorganization of substituents on their double bonds between two olefins in the presence of a catalyst is known as the olefin metathesis reaction. The use of metathesis reaction for polymer synthesis is called olefin metathesis polymerization.
Ruthenium-based Grubbs catalyst is the most commonly used catalyst for olefin metathesis polymerization. Grubbs catalyst consists...
2.2K
Polymer Classification: Architecture01:14

Polymer Classification: Architecture

Polymers are classified as linear or branched on the basis of their chain architecture. The polymer chains in linear polymers have a long chain-like structure with minimal to no branching at all. Even if a polymer features large substituent groups on the monomer, which appear as branches to the skeleton, it is not considered a branched polymer. A branched polymer contains secondary polymer chains that arise from the main polymer chain. The branching occurs when the polymer growth shifts from...
2.8K
Polymer Classification: Stereospecificity01:26

Polymer Classification: Stereospecificity

Polymerization generates chiral centers along the entire backbone of a polymer chain. Accordingly, the stereochemistry of the substituent group has a significant effect on polymer properties. Polymers formed from monosubstituted alkene monomers feature chiral carbons at every alternate position in the polymer backbone. Relative to the predominant orientation of substituents at the adjacent chiral carbons, the polymer can exist in three different configurations: isotactic, syndiotactic, and...
2.5K
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
2.3K
Olefin Metathesis Polymerization: Ring-Opening Metathesis Polymerization (ROMP)01:16

Olefin Metathesis Polymerization: Ring-Opening Metathesis Polymerization (ROMP)

Ring-opening metathesis polymerization or ROMP involves strained cycloalkenes as starting materials. The mechanism of ROMP proceeds by reacting cycloalkene with Grubbs catalyst to give metallacyclobutane intermediate which undergoes a ring-opening reaction to form new carbene. The new carbene reacts with another molecule of cycloalkene. Repetition of these steps leads to the formation of an unsaturated open-chain polymer product. All these steps are reversible, however, relieving the ring...
2.7K