Lignin particles as green pore-forming agents for the fabrication of microporous polysulfone membranes

Templating polymeric membranes with micro-nano-scaled solid materials is an effective method to simultaneously improve the water flux and retention ratio. However, the fabrication of a green, recyclable, and size-controlled template material remains a challenge. Here, a new green pore-forming agent, lignin particles (LP), was developed to prepare porous polysulfone (PSF) membranes via the phase inversion technique. A series of LP have uniform sizes from ~200 nm to ~1800 nm. The performances of the templated PSF membranes cast at different sizes and contents of LP were examined for their surface and crosssection morphologies. The LP-templated PSF membranes displayed a remarkable enhancement in flux, porosity, and moisture content. Particularly, the PSF membranes cast with LP from ~200 to 1800 nm broke the traditional trade-off to a certain degree, which possessed stable retentions of bovine serum albumin (> 85 %) and significantly improved water flux (174.275 to 254.775 L m^-2 h^-1). In addition, the LP pore-forming agent is low-cost and environmentally friendly as it was prepared from industrial by-products and can be easily recycled. Overall, this study shows that lignin particles are green pore-forming agents that can be used for the fabrication of porous polymeric membranes with improved performance for water treatment.