Magnesium Ortho-Vanadate/Magnesium Oxide/Graphene Oxide Embedded through Cellulose Acetate-Based Films for Wound...

A multifunctional nano-films of cellulose acetate (CA)/magnesium ortho-vanadate (MOV)/magnesium oxide/graphene oxide wound coverage was fabricated. Through fabrication, different weights of the previously mentioned ingredients were selected to receive a certain morphological appearance. The composition was confirmed by XRD, FTIR, and EDX techniques. SEM micrograph of Mg₃(VO₄)₂/MgO/GO@CA film depicted that there was a porous surface with flattened rounded MgO grains with an average size of 0.31 µm was observed. Regarding wettability, the binary composition of Mg₃(VO₄)₂@CA occupied the lowest contact angle of 30.15 ± 0.8^o, while pure CA represents the highest one at 47.35 ± 0.4°. The cell viability % amongst the usage of 4.9 µg/mL of Mg₃(VO₄)₂/MgO/GO@CA is 95.77 ± 3.2%, while 2.4 µg/mL showed 101.54 ± 2.9%. The higher concentration of 5000 µg/mL exhibited a viability of 19.23%. According to optical results, the refractive index jumped from 1.73 for CA to 1.81 for Mg₃(VO₄)₂/MgO/GO@CA film. The thermogravimetric analysis showed three main stages of degradation. The initial temperature started from room temperature to 289 °C with a weight loss of 13%. On the other hand, the second stage started from the final temperature of the first stage and end at 375 °C with a weight loss of 52%. Finally, the last stage was from 375 to 472 °C with 19% weight loss. The obtained results, such as high hydrophilic behavior, high cell viability, surface roughness, and porosity due to the addition of nanoparticles to the CA membrane, all played a significant role in enhancing the biocompatibility and biological activity of the CA membrane. The enhancements in the CA membrane suggest that it can be utilized in drug delivery and wound healing applications.