Optimization of Process Parameters for Carbon Fiber Reinforced Polyamide 6 Composites Fabricated by Self-Resistance...

As an energy-saving and efficient composites-forming technology, the properties of carbon fiber self-resistance electric (SRE) heating technology still need to be improved, which is not conducive to the popularization and application of this technology. To deal with this problem, the SRE heating technology was combined with a compression molding process to form carbon-fiber-reinforced polyamide 6 (CF/PA 6) composite laminates in this study. Orthogonal experiments of three factors (temperature, pressure, and impregnation time) were designed to study the effect of process parameters on the impregnation quality and mechanical properties of CF/PA 6 composite laminates and to obtain the optimized set of process parameters. Furthermore, the effect of the cooling rate on crystallization behaviors and mechanical properties of laminates was studied according to the optimized settings. The results show that the laminates possess a good comprehensive forming quality under process parameters using a forming temperature of 270 °C, forming pressure of 2.5 MPa, and an impregnation time of 15 min. The ununiform impregnation rate is due to the ununiform temperature field in the cross-section. When the cooling rate decreases from 29.56 °C/min to 2.64 °C/min, the crystallinity of the PA 6 matrix increases from 25.97% to 37.22%; the α-phase of the matrix crystal phase also increases significantly. The effect of the cooling rate on crystallization properties also further affects the impact properties; laminates with a faster cooling rate have stronger impact resistance.