Understanding the Degradation of Methylenediammonium and Its Role in Phase-Stabilizing Formamidinium Lead Triiodide

Formamidinium lead triiodide (FAPbI₃) is the leading candidate for single-junction metal-halide perovskite photovoltaics, despite the metastability of this phase. To enhance its ambient-phase stability and produce world-record photovoltaic efficiencies, methylenediammonium dichloride (MDACl₂) has been used as an additive in FAPbI₃. MDA²⁺ has been reported as incorporated into the perovskite lattice alongside Cl^-. However, the precise function and role of MDA²⁺ remain uncertain. Here, we grow FAPbI₃ single crystals from a solution containing MDACl₂ (FAPbI₃-M). We demonstrate that FAPbI₃-M crystals are stable against transformation to the photoinactive δ-phase for more than one year under ambient conditions. Critically, we reveal that MDA²⁺ is not the direct cause of the enhanced material stability. Instead, MDA²⁺ degrades rapidly to produce ammonium and methaniminium, which subsequently oligomerizes to yield hexamethylenetetramine (HMTA). FAPbI₃ crystals grown from a solution containing HMTA (FAPbI₃-H) replicate the enhanced α-phase stability of FAPbI₃-M. However, we further determine that HMTA is unstable in the perovskite precursor solution, where reaction with FA⁺ is possible, leading instead to the formation of tetrahydrotriazinium (THTZ-H⁺). By a combination of liquid- and solid-state NMR techniques, we show that THTZ-H⁺ is selectively incorporated into the bulk of both FAPbI₃-M and FAPbI₃-H at ∼0.5 mol % and infer that this addition is responsible for the improved α-phase stability.