Bioresorbable Poly (L-Lactic Acid) Flow Diverter Versus Cobalt-Chromium Flow Diverter: In Vitro and In Vivo Analysis
Natsuhi Sasaki1, Akira Ishii1, Shinichi Yagi2
1Department of Neurosurgery, Kyoto University Graduate School of Medicine, Japan (N.S., A.I., H.N., R.A., M.O., Y.A., H.T., S.M.).
Background:
Permanent metallic flow diverter (FD) implantation for treatment of intracranial aneurysms requires antiplatelet therapy for an unclear duration and restricts postprocedural endovascular access. Bioresorbable FDs are being developed as a solution to these issues, but the biological reactions and phenomena induced by bioresorbable FDs have not been compared with those of metallic FDs.
Methods:
We have developed a bioresorbable poly (L-lactic acid) FD (PLLA-FD) and compared it with an FD composed of cobalt-chromium and platinum-tungsten (CoCr-FD). FD mechanical performance and in vitro degradation of the PLLA-FD were evaluated. For in vivo testing in a rabbit aneurysm model, FDs were implanted at the aneurysm site and the abdominal aorta in the PLLA-FD group (n=21) and CoCr-FD group (n=15). Aneurysm occlusion rate, branch patency, and thrombus formation within the FD were evaluated at 3, 6, and 12 months. Local inflammation and neointima structure were also evaluated.
Results:
Mean strut, porosity, and pore density for the PLLA-FD were 41.7 μm, 60%, and 20 pores per mm2, respectively. The proportion of aneurysms exhibiting a neck remnant or complete occlusion did not significantly differ between the groups; however, the complete occlusion rate was significantly higher in the PLLA-FD group (48% versus 13%; P=0.0399). Branch occlusion and thrombus formation within the FD were not observed in either group. In the PLLA-FD group, CD68 immunoreactivity was significantly higher, but neointimal thickness decreased over time and did not significantly differ from that of the CoCr-FD at 12 months. Collagen fibers significantly predominated over elastic fibers in the neointima in the PLLA-FD group. The opposite was observed in the CoCr-FD group.
Conclusions:
The PLLA-FD was as effective as the CoCr-FD in this study and is feasible for aneurysm treatment. No morphological or pathological problems were observed with PLLA-FD over a 1-year period.
More Related Videos
08:44An In Vitro Hemodynamic Loop Model to Investigate the Hemocytocompatibility and Host Cell Activation of Vascular Medical Devices
Published on: August 21, 2020
09:41Hemocompatibility Testing of Blood-Contacting Implants in a Flow Loop Model Mimicking Human Blood Flow
Published on: March 5, 2020