Control over Phase Transformations in a Family of Flexible Double Diamondoid Coordination Networks through Linker...

In this work, we present the first metal-organic framework (MOF) platform with a self-penetrated double diamondoid (ddi) topology that exhibits switching between closed (nonporous) and open (porous) phases induced by exposure to gases. A crystal engineering strategy, linker ligand substitution, was used to control gas sorption properties for CO₂ and C3 gases. Specifically, bimbz (1,4-bis(imidazol-1-yl)benzene) in the coordination network X-ddi-1-Ni ([Ni₂(bimbz)₂(bdc)₂(H₂O)], H₂bdc = 1,4-benzenedicarboxylic acid) was replaced by bimpz (3,6-bis(imidazol-1-yl)pyridazine) in X-ddi-2-Ni ([Ni₂(bimpz)₂(bdc)₂(H₂O)]). In addition, the 1:1 mixed crystal X-ddi-1,2-Ni ([Ni₂(bimbz)(bimpz)(bdc)₂(H₂O)]) was prepared and studied. All three variants form isostructural closed (β) phases upon activation which each exhibited different reversible properties upon exposure to CO₂ at 195 K and C3 gases at 273 K. For CO₂, X-ddi-1-Ni revealed incomplete gate-opening, X-ddi-2-Ni exhibited a stepped isotherm with saturation uptake of 3.92 mol·mol^-1, and X-ddi-1,2-Ni achieved up to 62% more gas uptake and a distinct isotherm shape vs the parent materials. Single-crystal X-ray diffraction (SCXRD) and in situ powder X-ray diffraction (PXRD) experiments provided insight into the mechanisms of phase transformation and revealed that the β phases are nonporous with unit cell volumes 39.9, 40.8, and 41.0% lower than the corresponding as-synthesized α phases, X-ddi-1-Ni-α, X-ddi-2-Ni-α, and X-ddi-1,2-Ni-α, respectively. The results presented herein represent the first report of reversible switching between closed and open phases in ddi topology coordination networks and further highlight how ligand substitution can profoundly impact the gas sorption properties of switching sorbents.