Carbon Nanotube-, Boron Nitride-, and Graphite-Filled Polyketone Composites for Thermal Energy Management

In order to improve the thermal conductivity of 30 wt % synthetic graphite (SG)-filled polyketones (POKs), conductive fillers such as multiwall carbon nanotubes (CNTs) and hexagonal boron nitride (BN) were used in this study. Individual and synergistic effects of CNTs and BN on 30 wt % synthetic graphite-filled POK on thermal conductivity were investigated. 1, 2, and 3 wt % CNT loading enhanced the in-plane and through-plane thermal conductivities of POK-30SG by 42, 82, and 124% and 42, 94, and 273%, respectively. 1, 2, and 3 wt % BN loadings enhanced the in-plane thermal conductivity of POK-30SG by 25, 69, and 107% and through-plane thermal conductivity of POK-30SG by 92, 135, and 325%. It was observed that while CNT shows more efficient in-plane thermal conductivity than BN, BN shows more efficient through-plane thermal conductivity. The electrical conductivity value of POK-30SG-1.5BN-1.5CNT was obtained to be 1.0 × 10^-5 S/cm, the value of which is higher than that of POK-30SG-1CNT and lower than that of POK-30SG-2CNT. While BN loading led to a higher heat deflection temperature (HDT) than CNT loading, the hybrid fillers of BNT and CNT led to the highest HDT value. Moreover, BN loading led to higher flexural strength and Izod-notched impact strength values than CNT loading.