Fit and fatigue behavior of CAD-CAM lithium disilicate crowns

New computer-aided design and computer-aided manufacturing (CAD-CAM) lithium disilicate glass-ceramics have been marketed. However, information concerning their biomechanical behavior is lacking.

The purpose of this in vitro study was to compare the fit and fatigue behavior of two recently introduced CAD-CAM lithium disilicate materials with the standard IPS e.max CAD ceramic and to investigate the effect of the thermal treatment for crystallization on crown fit.

Monolithic crowns (n=15) were milled from 3 CAD-CAM lithium disilicates: IPS e.max CAD (Ivoclar AG), Rosetta SM (Hass), and T-lithium (Shenzhen Upcera Dental Technology). Marginal and internal fit were evaluated using the replica technique before and after crystallization, and the fatigue behavior of the luted crowns was evaluated by the step-stress method. One-way ANOVA and the Tukey test were used to compare fit among the materials. Fatigue failure load was evaluated by the Kaplan-Meier and Mantel-Cox tests. The effect of crystallization on fit was evaluated with the paired t test (α=.05).

Marginal fit was different between IPS e.max CAD (74 μm) and Rosetta SM (63 μm) (P=.02). T-lithium was similar to the other ceramics (68 μm) (P>.05). Occlusal internal space was similar among all materials (P=.69). Fatigue failure loads of Rosetta SM (1160 N) and T-lithium (1063 N) were similar to IPS e.max CAD (1082 N) (P>.05). The fatigue failure load of Rosetta SM was higher than that of T-lithium (P=.04). Crystallization reduced the axial internal space of all materials (P<.05) without significantly affecting marginal fit (P>.05).

The fit and fatigue behavior of Rosetta SM and T-lithium were similar to that of IPS e.max CAD. Crystallization reduced the internal space of the crowns.