Multicore-shell MnO₂@Ppy@N-doped porous carbon nanofiber ternary composites as electrode materials for...

In this study, a multicore-shell ternary composite electrode material (MnO₂@Ppy@NPCNFs) with excellent electrochemical performances was prepared by using surface modification, in which core-shell Ppy@N-doped porous carbon nanofibers (Ppy@NPCNFs) with large specific surface area and high conductivity were used as the substrate (a multicore layer), and MnO₂ was loaded on the substrate by hydrothermal synthesis to form a shell layer, further improving the SC of electrode material. The parameters of hydrothermal growth of MnO₂ on Ppy@NPCNFs were explored by means of the control variable method and response surface methodology, and the optimal parameters were predicted and verified. Electrochemical test results showed that the SC of MnO₂@Ppy@NPCNFs prepared under the optimal reaction parameters was as high as 595.77 F g^-1, and its capacitance retention was 96.2 % after 1000 cycles. Moreover, a symmetric supercapacitor prepared with the optimal multicore-shell electrode showed an energy density of 9.36 Wh kg^-1 at a power density of 1000 W kg^-1 and a retention rate of 92.46 % after 1000 cycles, indicating the promising application of multicore-shell ternary composite electrode material in high-performance supercapacitors.