Oriented Plate-like KNbO₃ Polycrystals: Topochemical Mesocrystal Conversion and Piezoelectric and Photocatalytic...

KNbO₃ (KN) with a perovskite structure is an outstanding representative of lead-free piezoelectric materials, and its mesocrystals have broad application prospects in the fields of catalysis, energy storage, and conversion. However, the formation conditions of KN mesocrystals reported so far are difficult owing to their high aspect ratio and excellent preferred orientation. In this study, the solvothermal process was used successfully to prepare the flake-like potassium salt of Lindquist hexaniobate (K₈Nb₆O₁₉·10H₂O). Subsequently, the precursor niobate was calcined to prepare two-dimensional (2D) plate-like KN mesocrystals. The formation mechanism of the plate-like KN mesocrystals is further revealed from a paired topochemical mesocrystal conversion of K₈Nb₆O₁₉·10H₂O niobate. Finally, the microscopic piezoelectric and photocatalytic responses of the obtained plate-like KN mesocrystals were investigated. The high piezoelectric coefficient of plate-like KN mesocrystals implies that excellent charge separation promotes the photocatalytic performance of rhodamine B (RhB). This study provides a strategy for the efficient application of 2D oriented materials in the field of piezoelectricity and photocatalysis.