Development and Promotion of Concrete Strength at Initial 24 Hours

Knowing and promoting the strength development of concrete at an earlier age is essential for accelerating formwork circulation of the on-site construction and precast product manufacture. The strength development rate at earlier ages of less than the initial 24 h was investigated. The effect of measures of adding silica fume, calcium sulfoaluminate cement, and early strength agent on the strength development of earlier concrete at ambient temperatures of 10, 15, 20, 25, and 30 °C was studied. The microstructure and long-term properties were further tested. It is shown that the strength increases exponentially first and then logarithmically, different from what is commonly recognized. Increasing cement content exhibited a certain effect only above 25 °C. When the cement content increased from 420 to 460 kg/m³, the strength only increased from 6.2 to 6.7 MPa after 12 h at 25 °C. The early strength agent could increase the strength significantly, the strength could be increased from 6.4 to 10.8 MPa after 20 h at 10 °C and from 7.2 to 20.6 MPa after 14 h at 20 °C. All measures for promoting earlier strength did not have an evident negative effect. The results could be potentially referred for the formwork removal at a suitable moment.