Influence of Aging Treatment Regimes on Microstructure and Mechanical Properties of Selective Laser Melted 17-4 PH...

Aging is indispensable for balancing the strength and ductility of selective laser melted (SLM) precipitation hardening steels. This work investigated the influence of aging temperature and time on the microstructure and mechanical properties of SLM 17-4 PH steel. The 17-4 PH steel was fabricated by SLM under a protective argon atmosphere (99.99 vol.%), then the microstructure and phase composition after different aging treatments were characterized via different advanced material characterization techniques, and the mechanical properties were systematically compared. Coarse martensite laths were observed in the aged samples compared with the as-built ones, regardless of the aging time and temperature. Increasing the aging temperature resulted in a larger grain size of the martensite lath and precipitation. The aging treatment induced the formation of the austenite phase with a face-centered cubic (FCC) structure. With prolonged aging treatment, the volume fraction of the austenite phase increased, which agreed with the EBSD phase mappings. The ultimate tensile strength (UTS) and yield strength gradually increased with increasing aging times at 482 °C. The UTS reached its peak value after aging for 3 h at 482 °C, which was similar to the trend of microhardness (i.e., UTS = 1353.4 MPa). However, the ductility of the SLM 17-4 PH steel decreased rapidly after aging treatment. This work reveals the influence of heat treatment on SLM 17-4 steel and proposes an optimal heat-treatment regime for the SLM high-performance steels.