Synthesis and application of alginate-nanocellulose composite beads for defluoridation process in a batch and...

Electronegative Fluorine has great reactivity and it exists as organic or inorganic fluoride compounds. Biosorption feasibility of fluoride onto alginate-cellulose composites was investigated in this study. Extracted cellulose has been utilized to synthesize calcium alginate impregnated composite beads for fluoride remediation process in batch and fluidized-bed reactors. Physiochemical characteristics were analyzed by FTIR, SEM, TGA and BET. From the BET properties analysis, the surface area of prepared composite beads was 87.13 m²/g. The point zero charge (PZC) value of composite beads was attained at pH 7.32. The relationship between biosorption efficiency and independent variables have been observed to evaluate the effects on the fluoride biosorption efficiency of composites and its components. The hypothetical development of the removal technique has been explained using various nonlinear model-fitting methods to evaluate Isotherm study, bio-sorption Kinetics, Thermodynamic parameters and Mass transfer study. Maximum monolayer adsorption capacity (q_m) obtained by following Langmuir model for fluoride removal was found to be 23.809 mg/g at 30 °C using adsorbent dosage of 2 g/L for an initial fluoride concentration of 6 mg/L. The optimized condition for fluoride adsorption experiment was observed by evaluating response surface methodology (RSM) was pH-5.67, dose 1.89 g/L and time 85.71 min and removal was found as 82.79%. Experimental data of fluidized-bed study were evaluated by designing mathematical modeling. Fluidization velocities was adjusted in between U_mf and 2U_mf for optimizing external mass transfer and adsorbent loss. Regeneration study of fluoride loaded biosorbent and cost analysis of composite production have been estimated.