Effect of sulfonation time on physicochemical, osteogenic, antibacterial properties and biocompatibility of carbon
Jingjing Su1, Qingshi Wu2, Xiaojie Xing1
1Fujian Key Laboratory of Oral Diseases & Fujian Provincial Engineering Research Center of Oral Biomaterial & Stomatological Key Lab of Fujian College and University, School and Hospital of Stomatology, Fujian Medical University, Fuzhou, 350000, China.
Abstract:
The carbon fiber reinforced polyetheretherketone (CFR-PEEK) has been increasingly used in orthopedics dentistry due to its excellent biocompatibility and mechanical properties. However, the biological inertness and poor antibacterial activity limit its clinical applications. This paper focused on the performances of CFR-PEEK with porous morphology that were exposed to different sulfonation periods (1, 3, 5, and 10 min, corresponding to CP-S1, CP-S3, CP-S5, and CP-S10, respectively). Residual sulfuric acid was removed by acetone rinsing, NaOH immersion, and hydrothermal treatment before in vitro and in vivo studies. The results showed some significant difference in the physicochemical properties, including energy dispersive X-ray spectroscopy (EDS) map of sulfur atoms, X-ray photoelectron spectroscopy (XPS) of valences of sulfur ions, Fourier transformation infrared spectroscopy (FTIR), hydrophilicity, hardness, and elastic modulus among CP-S3, CP-S5, and CP-S10. However, CP-S5 and CP-S10 were more effective in promoting the proliferation, adhesion, and osteogenic differentiation of seeded bone mesenchymal stem cells (BMSCs) and growth inhibition of S. aureus and P. gingivalis compared with other groups. Furthermore, the CP-S5 and CP-S10 samples achieved better cranial bone repair than the non-sulfonation group in a rat model. Therefore, it can be inferred that both 5 and 10 min are viable sulfonation durations for 30% CFR-PEEK. These findings provide a theoretical basis for developing CFR-PEEK for clinical applications.