Effects of Different Primers on the Bond Strength to Properly and Excessively Etched Ceramic-coated Zirconia

To determine the effects of various primers on the immediate and long-term bond strength of ceramic-coated ultratranslucent zirconia that is properly or excessively etched.

Ceramic-coated zirconia plates were etched with 9.5% hydrofluoric acid (HF) for 2 or 5 minutes, after which the surface morphology and elemental composition were examined. The etched specimens were treated with different primers including methacryloyloxydecyl dihydrogen phosphate (MDP)-only containing primer, silane-only containing primer, MDP and silane-containing ceramic primer as well as MDP and silane-containing adhesive system. For surface contact angle and shear bond strength (SBS) data, the difference between groups was evaluated by one-way analysis of variance (ANOVA) and three-way ANOVA factorial analysis, respectively. The statistical significance level of 0.05 was set and the Tukey test and the Dunnett-T3 test were used for post-hoc multiple comparisons.

Excessive etching (9.5% HF for 5 minutes) led to overconsumption of the glass layer and exposure of zirconia substrate compared to proper etching (9.5% HF for 2 minutes). Among different primers, the surface contact angle of the silane-only containing primer group was the lowest. The silane-only containing primer and MDP and silane-containing ceramic primer produced higher shear bond strength of properly and excessively etched ceramic-coated zirconia, respectively, both before and after thermal aging.

The silane-only containing primer and MDP and silane-containing primer can obtain better immediate and long-term shear bond strength for properly and excessively etched ceramic-coated zirconia, respectively.