Scanning Electron Microscopic Evaluation of Surface Defects of Remover Retreatment File After Single and Multiple Uses
Published on: October 11, 2024
Apically extruded debris, canal transportation, and shaping ability of nickel-titanium instruments on contracted
Qinqin Zhang1, Jingyi Gu1, Jiadi Shen1
1Department of Endodontics, Affiliated Stomatological Hospital of Nanjing Medical University.
Purpose:
Apically extruded debris, canal transportation and shaping ability were compared between contracted endodontic cavities (CECs) and traditional endodontic cavities (TECs) after instrumentation with XP-endo Shaper (XPS), ProTaper Gold (PTG), ProTaper for hand-use (HPT) and Hero Shaper.
Methods:
The CECs or TECs groups were sub-divided into 24 groups according to root canal morphology and nickel-titanium (Ni-Ti) instruments. The weight of apically extruded debris was calculated using the Myers and Montgomery model. Pre- and postoperative images of teeth were scanned using micro-CT and the three-dimensional models were constructed and compared.
Results:
Under CECs or TECs, XPS and PTG produced less apical debris and formed less canal transportation than HPT and Hero Shaper (P < 0.05). XPS group under CECs extruded less apical debris than that under TCEs for round canals with curvature of 20°-35° (P < 0.05). The centering ratios of four tested instruments were higher under TECs than those under CECs (P < 0.05). The HPT and Hero Shaper had more transportation under CECs than that under TCEs (P < 0.05). No statistical difference was found regarding shaping ability among all the groups.
Conclusion:
Under CECs, XPS preserves the original root canal anatomy, meanwhile it produces less apical debris than the other instruments.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
05:30Roughness Impact of Piezoelectric Dental Scaler on Two Distinct Flowable Composite Filling Materials
Published on: January 10, 2025