Development of UV-Irradiated PADC and Improvement of Etching for Reducing Experimental Time

PADC is well known as a highly sensitive solid-state nuclear track detector. A proposal is for a radiation education method that utilizes these characteristics. A significant issue in the proposed educational method using PADC is the time-consuming etching process. This study attempted to reduce etching time by using a homemade PADC. The experimental results have revealed that the homemade PADC achieves faster etch pit enlargement compared to BARYOTRAK (commercial PADC). An attempt was made to enlarge etch pit diameters rapidly by irradiating UV at a wavelength of 253.7 nm and etching with NaOHaq/ethanol solution. The results revealed that UV irradiation at a wavelength of 253.7 nm, after etching, resulted in etch pit diameters several times larger than those obtained in conventional methods within the same etching time. Therefore, UV irradiation and short-time etching with NaOHaq/ethanol solution proved to be effective. This study also investigated the effects of fading on the PADC during its storage period after UV irradiation. The experimental results confirmed that the etch pit diameters shrank by approximately 30% after 2 months of storage. However, considering the enlargement effect of the etch pit diameters due to UV irradiation, it can be concluded that UV irradiation is practical for radiation education experiments.