Tuning Oxide Properties by Oxygen Vacancy Control During Growth and Annealing
Published on: June 9, 2023
Low-Temperature Enhancement-Mode Amorphous Oxide Thin-Film Transistors in Solution Process Using a Low-Pressure
Won Park1, Jun-Hyeong Park1, Jun-Su Eun1
1School of Electronic and Electrical Engineering, Kyungpook National University, Daegu 41566, Republic of Korea.
Abstract:
The interest in low processing temperature for printable transistors is rapidly increasing with the introduction of a new form factor in electronics and the growing importance of high throughput. This paper reports the fabrication of low-temperature-processable enhancement-mode amorphous oxide thin-film transistors (TFTs) using the solution process. A facile low-pressure annealing (LPA) method is proposed for the activation of indium oxide (InOx) semiconductors at a significantly low processing temperature of 200 °C. Thermal annealing at a pressure of about ~10 Torr induces effective condensation in InOx even at a low temperature. As a result, the fabricated LPA InOx TFTs not only functioned in enhancement mode but also exhibited outstanding switching characteristics with a high on/off current ratio of 4.91 × 109. Furthermore, the LPA InOx TFTs exhibit stable operation under bias stress compared to the control device due to the low concentration of hydroxyl defects.